C. Samsung Reliablility Test and Judgement Condition

Capacitance

Within specified tolerance

Tan δ (DF)

0.025 max.

Insulation

10,000Mohm or 500Mohm×㎌

Rated Voltage

60~120 sec.

Resistance

Whichever is smaller

Appearance

No abnormal exterior appearance

Microscope (×10)

Withstanding

No dielectric breakdown or

of the rated voltage

Voltage

mechanical breakdown

Temperature

X7R

Characteristics

(From-55℃ to 125℃, Capacitance change should be within ±15%)

Adhesive Strength

No peeling shall be occur on the

500g·f, for 10±1 sec.

of Termination

terminal electrode

Bending Strength

Capacitance change :

within ±12.5%

Bending to the limit (1㎜)

with 1.0mm/sec.

Solderability

More than 75% of terminal surface

SnAg3.0Cu0.5 solder

is to be soldered newly

245±5

℃, 3±0.3sec.

(preheating : 80~120

℃ for 10~30sec.)

Resistance to

Capacitance change :

within ±7.5%

Solder pot : 270±5

℃, 10±1sec.

Soldering Heat

Tan δ, IR : initial spec.

Vibration Test

Capacitance change :

within ± 5%

Amplitude : 1.5mm

Tan δ, IR : initial spec.

From 10

㎐ to 55㎐ (return : 1min.)

2hours × 3 direction (x, y, z)

Moisture

Capacitance change :

within ±12.5%

With rated voltage

Resistance

Tan δ :

0.05 max

40±2

℃, 90~95%RH, 500+12/-0hrs

IR :

500Mohm or 25Mohm × ㎌

Whichever is smaller

High Temperature

Capacitance change :

within ±12.5%

With

of the rated voltage

Resistance

Tan δ :

0.05 max

Max. operating temperature

IR :

1,000Mohm or 50Mohm × ㎌

1000+48/-0hrs

Whichever is smaller

Temperature

Capacitance change :

within ±7.5%

1 cycle condition

Cycling

Tan δ, IR : initial spec.

Min. operating temperature

→

25

℃

→

Max. operating temperature

→

25

℃

5 cycle test

※ The reliability test condition can be replaced by the corresponding accelerated test condition.

D. Recommended Soldering method :

Reflow ( Reflow Peak Temperature : 260+0/-5

℃, 10sec. Max )

Product specifications included in the specifications are effective as of March 1, 2013.

Please be advised that they are standard product specifications for reference only.

We may change, modify or discontinue the product specifications without notice at any time.

So, you need to approve the product specifications before placing an order.

Should you have any question regarding the product specifications,

please contact our sales personnel or application engineers.

250%

200%

Judgement

Test condition

1㎑ ±10% / 1.0±0.2Vrms

*A capacitor prior to measuring the capacitance is heat

treated at 150℃+0/-10℃ for 1 hour and maintained in

ambient air for 24±2 hours.

2